PROTAC balistické ochranné ocele

 

  • Certifikované a testované v súlade s normami VPAM APR 2006 a STANAG 4569 AEP 55

  • Rôzne úrovne ochrany pre celý rad použití

  • Popredajná podpora (odporúčania na zváranie a ohýbanie, poloprodukty)

  • Minimálne objednané množstvo je 10 t na triedu v rôznej hrúbke

  • Krátke dodacie lehoty - od 6-8 týždňov

  • Veľkoplošné platne, napr. 8 x 2,5 m pre pohodlie zákazníka

 

 

PROTAC 430 PROTAC 500 PPROTAC 550 PROTAC 600
Standard antibalistic
protection steel, with
excellent toughness
Standard 500HB grade, with
good bending and welding
characteristics
Advanced Q&T armour
plate with higher hardness
and excellent toughness
High hardness
and toughness
for best performance
H: 400-450 HB H: 480-530 HB H: 514-555 HB H: 600-650 HB

 

 

PROTAC 430
CHEMICAL COMPOSITION
PROTAC Thickness [mm] C Si Mn P S Cr Ni Mo B
430 6.5 - 60 0.30 1.1 1.2 0.02 0.003 0.8 1.1 0.5 0.004
All value are in max. %
 
TYPICAL MECHANICAL PROPERTIES
  Tensile properties* Impact properties* Hardness
PROTAC Thickness [mm] Yield strength Rp 0,2 [MPa] Tensile strength Rm [MPa] Elongation A5 [%] Test temperature [°C] Impact energy Charpy V transverse [J] HB
430 6.5 - 60 1,100 1,200 10 -20 | +20 30 | 45 400 - 450

 

 

PROTAC 500
CHEMICAL COMPOSITION
PROTAC Thickness [mm] C Si Mn P S Cr Ni Mo B
500 6.5 - 60 0.30 1.3 0.8 0.02 0.003 0.8 1.5 0.5 0.004
All value are in max. %
 
TYPICAL MECHANICAL PROPERTIES
  Tensile properties* Impact properties* Hardness
PROTAC Thickness [mm] Yield strength Rp 0,2 [MPa] Tensile strength Rm [MPa] Elongation A5 [%] Test temperature [°C] Impact energy Charpy V transverse [J] HB
500 6.5 - 60 1,200 1,700 10 -20 25 480 - 530

 

 

PROTAC 550
CHEMICAL COMPOSITION
PROTAC Thickness [mm] C Si Mn P S Cr Ni Mo B
550 6.5 - 60 0.33 1.0 0.8 0.02 0.003 0.8 3.5 0.5 0.004
All value are in max. %
 
TYPICAL MECHANICAL PROPERTIES
  Tensile properties* Impact properties* Hardness
PROTAC Thickness [mm] Yield strength Rp 0,2 [MPa] Tensile strength Rm [MPa] Elongation A5 [%] Test temperature [°C] Impact energy Charpy V transverse [J] HB
550 6.5 - 60 1,300 1,800 10 -20 20 514 - 555

 

 

PROTAC 600
CHEMICAL COMPOSITION
PROTAC Thickness [mm] C Si Mn P S Cr Ni Mo B
600 6.5 - 60 0.42 1.0 0.8 0.02 0.003 0.9 3.5 0.5 0.004
All value are in max. %
 
TYPICAL MECHANICAL PROPERTIES
  Tensile properties* Impact properties* Hardness
PROTAC Thickness [mm] Yield strength Rp 0,2 [MPa] Tensile strength Rm [MPa] Elongation A5 [%] Test temperature [°C] Impact energy Charpy V transverse [J] HB
600 6.5 - 60 1,500 2,100 9 -40 20 570 - 650